OSA II knife, handmade by master Pavel Honcharenko, steel K110™ in laminate, 61 HRC
- Brand: Студія ножів ручної роботи Павла Гончаренка
- Product Code: ОСА ІІ - ніж ручної роботи майстра Павла Гончаренка
| Загальна довжина клинка mm: | 275±05 mm |
| Матеріал леза | Blade steel - Austrian high-carbon k110 Bohler-Uddeholm AG in a laminate of the same k110 through brass and two layers of nickel. Blade by Roma Cherniak |
| Твердість клинка (метал): | Hardness - the hardness of the central layer is 61 HRC |
| Матеріал руків'я: | Carbon, neuselber, micarta, stabilized maple sap, mosaic binding tube and foam. Strap made of leather cord 3 mm, bead made of stabilized maple cap |
| Довжина леза | 140±05 mm |
- Availability: Під замовлення
Available Options
Description
SPECIFICATIONS:
The name of the knife: OSA II exclusive collector's knife handmade by studio master Pavlo Honcharenko, order to buy in Ukraine (K110™ steel in a laminate of stainless steel n690 through nickel, 61 HRC)
Brand: Pavlo Honcharenko's Handmade Knives Studio
Blade material: Blade steel - Austrian high-carbon k110 Bohler-Uddeholm AG in a laminate of the same k110 through brass and two layers of nickel. Blade by Roma Cherniak
Steel sheet: One-piece cast, through-mounting on screed and resin
Blade sharpening angle: Sharpened at 34-35 degrees
Descents: Straight
Reduction: 0.1-0.2 mm
Blade sharpening: Saber double-sided knife ready for work.
Blade hardness: Hardness of the central layer is 61 HRC
Total length: 275 mm
Blade length: 140 mm
Blade width: 33mm
Blade thickness: 4.0 mm
Handle length: 135 mm
Handle thickness: 31 mm
Grinding of the blade: The finish of the blade is machine satin 600 grit
Bolster (guard) and back material: Guard and back made of carbon
Handle: Carbon, neuselber, micarta, stabilized maple sap, mosaic binding tube and foam. Strap made of leather cord 3 mm, bead made of stabilized maple cap
Handle color: Wasp
Impregnation of the handle: Yes
Handle cover: Yes
Hole for a shoelace (for a lanyard): Yes
Sheath: Birch wood is tinted, calf leather is chaprak. Italian vegetable-tanned genuine leather, hand-stitched with waxed thread, finished with a water-repellent finish, impregnated with protective solutions, stitched with waxed thread. Manual embossing of the invoice. The pendant is removable, free, hybrid insert, bead - amber.
Knife Condition: New
Price: Listed with scabbard.
Model: OSA II exclusive collector's knife handmade by studio master Pavlo Honcharenko, order to buy in Ukraine (K110™ steel in a laminate of stainless steel n690 through nickel, 61 HRC)
Model number: 127
Country of birth: Ukraine
Craftsman: Master Pavlo Honcharenko, Ivankiv, Ukraine Pavlo Honcharenko's Handmade Knives Studio
Best use: Hunting, cutting, cutting
Knife condition: new
The price is indicated together with the scabbard.
A sharpened knife is not a cold weapon.
Our knives are very sharp, so be very careful when opening and handling them. We are not responsible for any injuries resulting from the use of our knives.
Our products are intended for legal use only by responsible buyers. We will not sell our products to anyone under the age of 18.
Availability changes regularly, after confirming your order we will notify you of availability or when the item is ready. The product may differ slightly from the one shown in the photo.
K110 steel for knives - features, pros and cons
At the moment, there are many possible materials for the production of knives. Depending on the purpose of production, different materials are used. Moreover, the content of the main substances of different grades of steel can differ significantly. The most typical grades of steel are high-carbon types of steel. Among them, you can find many types of materials that differ among themselves in the number of additional elements. One of the best grades of steel for hunting knives is K1100 from the Austrian company Böhler.
Composition and features
Böhler K110 steel is a high-carbon composition with a high chromium content. The metal is stamped by the method of cold stamping. Metal is produced by one of the largest metallurgical concerns in the world. Factories are located in Europe, North and South America.
In the production of K110, the technology of electroslag remelting is used. Due to this, the quality of the material increases significantly. Due to the presence of various undesirable impurities, serious defects may appear during mechanical forging. To avoid this, the method of electroslag remelting is used. During electroslag remelting, before the start of hardening, the melt is passed through a layer of special slag, which removes foreign elements from the molten metal, such as phosphorus, sulfur, and much more.
The method of electroslag remelting provides the final result with low levels of segregation, purity and homogeneity of the structure. In Böhler K110, the percentage of harmful impurities is significantly reduced and the compounds of metals and non-metals with carbon are evenly distributed.
Therefore, such a metal has a complex composition and is able to withstand even very thin corners during forging. One of the main advantages is extremely high strength and viscosity. It is preferable to harden such material in the air. If necessary, the nitriding method is used. Böhler K100 is used for forging knife products of the medium and high price segment.
Metal composition:
- It contains 1.5% carbon, which provides higher strength and hardness.
- Chromium content is 12%. This metal provides an increased ability of steel to be hardened, resistance to rusting and wear.
- Molybdenum 0.8% is used for the production of high-speed steel. It significantly increases the rigidity of the blade, makes it resistant to high temperatures.
- The percentage share of vanadium is 1%. This chemical element has high strength. Strengthens the elasticity characteristics of the material and makes it resistant to various aggressive environments.
- Manganese - 0.35%. Manganese is used during smelting. It significantly increases the hardness of the material. A characteristic feature of manganese is that various objects requiring high strength are made from steel with a high content of the chemical element. For example, safes, rails and much more.
- Boehler K110
Main advantages
Any steel is an alloy of iron and carbon, but their ratio in the substance will directly affect the characteristics of the finished product. This type of material is produced by electroslag remelting. And due to the high content of impurities, the increased strength of the material is formed.
The main advantages of K110 steel from Böhler include:
The main requirement that applies to all knives is sharpening. However, the sharper you sharpen the knife, the faster it will dull. However, this rule does not apply to K110 knives. Due to the high concentration of chromium in this steel, the resistance to wear is significantly increased. Therefore, the cutting edge will always be sharp. However, the use of such impurities reduces corrosion resistance. Although the knife will not rust very quickly.
The presence of a high percentage of molybdenum in the composition provides the material with the uniformity and homogeneity of steel. This is very important for a knife. A small amount of vanadium increases the strength and durability of the material, and manganese in contact with chromium significantly increases strength.
After a lot of tests, it was found that even after a lot of processing bones and opening cans, practically no serrations appear on the blade. The blade continues to be able to cut the newspaper under its own weight.
Due to the combination of various impurities in the composition of the substance and the method of manufacturing steel, knives made of this material are distinguished by an extremely long service life.
Increased resistance of the blade to various aggressive environments, which include some internal organs of animals. Therefore, the knife will not darken and rust for a long time.
The main disadvantages
The disadvantages include:
It does not have high breaking strength. Therefore, it is undesirable to throw products, check for the ability to bend.
Blades from this material are usually made with a small size and a narrow focus. These are hunting knives specially prepared for processing carcasses. They are usually used by the inhabitants of Siberia and the North. However, the sword will be able to show its excellent properties only with competent preparation and sharpening. Otherwise, it is very easy to spoil the cutting edge. However, if such care is provided, knives with K110 will be equal to and the characteristics of blades made of higher quality steel.
Conclusion
K110 from Böhler from the Austrian manufacturer is one of the highest quality products for forging knives. Despite the demanding care of the blade and the mandatory condition to dry thoroughly after contact with water, a knife made of such metal will serve for a very long time in the right hands. Therefore, it is definitely worth buying K110 knives and tools from the Austrian manufacturer. They can last a long time.
*It should be remembered that if the knife is used for its intended purpose and with careful handling, the knife will serve you for a very, very long time.
Well, you can buy a Damascus steel knife on the порталі https://knife.net.ua/on our website or by contacting us by phone +380961711010.
Happy shopping! We will be glad to see you among our customers!
maple burl
A cap is a growth on a tree trunk, it has a much denser structure with a completely unique cut pattern.
The cap has high strength, the wood of the cap does not burn well, is well processed and polished.
The dimensions of the blanks are approximately 135-45-30 mm.
Bars of stabilized wood are great for creating standard through-mount and countersunk knife handles.
Also, stabilized maple sap is excellent for carving, creating miniatures, jewelry, as well as various pendants, amulets, toys and crafts.
It is convenient to work with a stabilized maple cap for both experienced craftsmen and beginners.
Stabilized wood of any color is straight, even bars of real wood - kapa maple impregnated with a special composition.
The wood stabilizer completely fills all small pores, thanks to which all the air and moisture come out of the wood, turning it into a polymerized bar of stabilized Karelian birch, only with improved properties.
Stabilized wood is many times heavier and much denser. It is not exposed to moisture, does not change its color under sunlight, remaining a much stronger and more reliable material.
All this makes stabilization an ideal material for creating objects that are exposed to all physical and climatic stresses - knife handles, cutters and various tools.
Stabilized maple sap is perfectly sanded, giving a surface as smooth as glass or stone. Without a coating in dry form, the stabilized bars have a faded appearance, but under the finishing compositions their bright deep texture is revealed.
For its unique beauty, the cap is called wooden malachite!
In general, the smaller the pattern and the larger the size of the cap, the more expensive it is.
The value of this unique material is told by a historical fact given in the book "Kapov Skrynka" (author Nadiya Perminova): "... in 1837, up to fifty rubles were paid for a cap growth of twenty pounds (a little more than 8 kg)... the same amount was estimated thoroughbred bull at an agricultural exhibition.
Today, on the world market, the price of veneered wood (solid and veneer) is several times higher than the price of any other, including: oak, elm, walnut, mahogany and any exotic species.
The unique combination of material properties, limited stocks and the uniqueness of the cap pattern in each product ultimately determined the universally recognized, high aesthetic value and corresponding consumer price of products made of this wood, which is used in the decoration of the most luxurious interiors.
CARBON - KNIFE HANDLES FROM THIS PREMIUM MATERIAL
One of the most prestigious and expensive materials for knife handles, in addition to titanium and expensive types of wood, is a type of carbon fiber, the so-called "carbon". The material is valued for its exceptional lightness, strength and aesthetic beauty.
Carbon (from the English carbon - carbon) is a polymer material with a composite composition, made of interwoven carbon fiber threads. These threads are made using epoxy resins. The average density of the material is from 1450 kg/m³ to 2000 kg/m³. The main difference between carbon and other polymers used in the manufacture of knives is its very low weight. It is the weight, together with exceptional strength, that gives carbon an advantage over other handle materials: G10 polymer, micarta, FRN plastic, etc. At the same time, according to specific strength characteristics, carbon exceeds structural steels. The main qualities of carbon are high tensile strength, resistance to high temperatures, aggressive environments, slight expansion when heated, high electrical conductivity. Another important feature of carbon is its natural black color obtained during production, which gives it a noble and elite look.